flexible PVC compound · Shore A 62–75 Soles & footwear
Antistatic, oil-resistant soling compounds that mould cleanly and bond to leather and textile alike.
Need a custom grade? Build your specification
At a glance
- Hardness
- Shore A 62–75
- Tensile
- 11.6–18.2MPa
- Elongation
- 310–341%
- Density
- 1.19–1.44g/cm³
Applications
Properties
- Excellent abrasion and slip resistance
- High antistatic properties
- High oil resistance
- Excellent moulding, smooth surface
- Good adhesion to leather and fabrics
Values
by grade.
Typical values from the FastPlast 2023 catalogue. We adapt hardness, density, colour and stabiliser to your specification, and supply samples for trials.
| Property | Method | Unit | NHMD037 | NHMP017 | NHMP107 | NHMP507 | NHMP607 | NHMP807 |
|---|---|---|---|---|---|---|---|---|
| Tensile strength | — | MPa | 17.8 | 17.9 | 18.2 | 12.5 | 12.3 | 11.6 |
| Elongation at break | IEC 811-1-1 | % | 325.6 | 340.6 | 320.6 | 328.4 | 322.6 | 310.1 |
| Density at 23 °C | ASTM D792 | g/cm³ | 1.21 | 1.19 | 1.23 | 1.32 | 1.32 | 1.44 |
| Hardness at 23 °C | ASTM D2240 | Shore A | 75 | 65 | 70 | 62 | 62 | 68 |
| Heat stability at 200 °C | IEC 811-3-2 | min | 70 | 70 | 68 | 64 | 63 | 60 |
| Use | Soles, welts | Soles, welts | Foam soles | Foam soles | Foam soles | Foam soles |
- NHMD037 Datasheet
- Tensile strength—
- 17.8 MPa
- Elongation at breakIEC 811-1-1
- 325.6 %
- Density at 23 °CASTM D792
- 1.21 g/cm³
- Hardness at 23 °CASTM D2240
- 75 Shore A
- Heat stability at 200 °CIEC 811-3-2
- 70 min
- Use
- Soles, welts
- NHMP017 Datasheet
- Tensile strength—
- 17.9 MPa
- Elongation at breakIEC 811-1-1
- 340.6 %
- Density at 23 °CASTM D792
- 1.19 g/cm³
- Hardness at 23 °CASTM D2240
- 65 Shore A
- Heat stability at 200 °CIEC 811-3-2
- 70 min
- Use
- Soles, welts
- NHMP107 Datasheet
- Tensile strength—
- 18.2 MPa
- Elongation at breakIEC 811-1-1
- 320.6 %
- Density at 23 °CASTM D792
- 1.23 g/cm³
- Hardness at 23 °CASTM D2240
- 70 Shore A
- Heat stability at 200 °CIEC 811-3-2
- 68 min
- Use
- Foam soles
- NHMP507 Datasheet
- Tensile strength—
- 12.5 MPa
- Elongation at breakIEC 811-1-1
- 328.4 %
- Density at 23 °CASTM D792
- 1.32 g/cm³
- Hardness at 23 °CASTM D2240
- 62 Shore A
- Heat stability at 200 °CIEC 811-3-2
- 64 min
- Use
- Foam soles
- NHMP607 Datasheet
- Tensile strength—
- 12.3 MPa
- Elongation at breakIEC 811-1-1
- 322.6 %
- Density at 23 °CASTM D792
- 1.32 g/cm³
- Hardness at 23 °CASTM D2240
- 62 Shore A
- Heat stability at 200 °CIEC 811-3-2
- 63 min
- Use
- Foam soles
- NHMP807 Datasheet
- Tensile strength—
- 11.6 MPa
- Elongation at breakIEC 811-1-1
- 310.1 %
- Density at 23 °CASTM D792
- 1.44 g/cm³
- Hardness at 23 °CASTM D2240
- 68 Shore A
- Heat stability at 200 °CIEC 811-3-2
- 60 min
- Use
- Foam soles